X153CrMoV12 Steel
- Fucheng Steel
- China
- 1 Month
- 2000 Tons/Month
X153CrMoV12 steel is suitable for making all kinds of cold stamping dies with large cross-section and complex shape, as well as cold cutting scissors and thread taking plates; Cold extrusion forming, trimming die, etc
X153CrMoV12 TOOL STEEL
| Smelting and Manufacture Method: | LF+VD+Forged |
| Delivery Condition: | Annealed |
| Delivery hardness： | ≤255 HBS |
| UT Test Standard: | Sep 1921-84 Class3 D/d,E/e |
X153CrMoV12 STEEL GRADE COMPARISON AND CHEMICAL COMPOSITION COMPARISON
| Standard/Steel Grade | Chemical Composition(%) | ||||||
| C | Si | Mn | Cr | Mo | V | ||
| ASTM | D2 | 1.40~1.60 | ≤0.60 | 0.10~0.60 | 11.00~13.00 | 0.70~1.20 | 0.50~1.10 |
| DIN/W-Nr. | X153CrMoV12/1.2379 | 1.45~1.60 | ≤0.60 | 0.20~0.60 | 11.00~13.00 | 0.70~1.00 | 0.70~1.00 |
| JIS | SKD11 | 1.40~1.60 | ≤0.40 | ≤0.60 | 11.00~13.00 | 0.80~1.20 | 0.20~0.50 |
APPLICATION
X153CrMoV12 tool steel is suitable for tool steel with complex deformation, all kinds of cold stamping dies with high wear resistance and long life, cold shear blades, and thread rolling plates; Cold extrusion forming, stretching film, beer stainless steel sheet and balance cutting die of high hardness materials, etc
X153CrMoV12 STEEL CHARACTERISTICS
X153CrMoV12
steel is a cold working die steel with high wear resistance and slight
deformation, with a carbon mass fraction of up to 1.5% and a chromium
mass fraction of up to 11.5%. The characteristic of this type of steel
is that its hardness can reach 60HRC through heat treatment. Therefore,
X153CrMoV12 steel is very suitable for manufacturing cold working molds with
large cross-sections, complex shapes, high impact resistance, and high
wear resistance requirements, such as silicon steel sheet punching
molds, cold cutting scissors, edge cutting molds, etc.
Due to its high carbon content and the presence of chromium, X153CrMoV12 steel has excellent wear resistance and wear resistance. In high-speed, high-temperature, and high-pressure working environments, it can maintain a stable working state for a long time and is not prone to fatigue and damage. This makes X153CrMoV12 steel exhibit excellent durability and reliability under heavy load and continuous working conditions.
X153CrMoV12 steel also has good strength and hardness, which is determined by its high carbon content. This characteristic enables X153CrMoV12 steel to maintain a stable shape and size under high impact and pressure, and is less prone to deformation or damage. Meanwhile, this also enables X153CrMoV12 steel to ensure the accuracy and repeatability of the mold when producing high-precision molds.
However, although X153CrMoV12 steel has excellent wear resistance and hardness, its ductility, toughness, and rust resistance are relatively weak. This to some extent limits its application in some special environments. Especially in environments with high humidity or corrosive gases, X153CrMoV12 steel may be more prone to rusting or corrosion. Therefore, when using X153CrMoV12 steel under these conditions, special protective measures need to be taken.
In addition, due to its high carbon content, it is best not to heat treat X153CrMoV12 steel if not required. Because the heat treatment process may cause changes in its internal structure, thereby affecting its hardness and wear resistance. If heat treatment is carried out unnecessarily, it may lead to a decrease in the performance of X153CrMoV12 steel, which cannot meet the requirements for use.
In the future development, with the advancement of technology and the improvement of processes, we hope that X153CrMoV12 steel can be applied in more fields, bringing more convenience and benefits to our lives and work. At the same time, we also look forward to developing more new materials to meet the needs of different fields and promote social progress and development.